Tuairisc

Bonded NdFeB magnets are manufactured by binding rapid-quenching NdFeB powder. The powder is mixed with resin to form a magnet by compression molding with epoxy or infection molding with nylon. The latter technique is particular effective in large volume production, though the magnetic value of products is lower than those made with compression molding because of their relatively lower density. Various shapes of high dimensional accuracy can be produced without further processing. Surface is treated by epoxy coating or nickel-plating to prevent corrosion

With different ratio of additives to NdFeB powder, magnetic properties of hybrid NdFeB magnets can be tuned in a wide range. Once the ratio is fixed, magnetic property fluctuation can still be limited in a narrow bank. Hybrid magnets will meet customerˇŻs specified properties.

Rapidly quenched NdFeB powder used for bonded magnets is multi grain with grain size of sub-micron. Powder is isotropic in magnetic properties, which results in flat increasing of remanence and intrinsic coercivity with applied field. Magnet can only be magnetized to saturation in high fields.

Advantages of Bonded Magnets
*Produced with high efficiency, stability and repeatability.
*Magnet and other part may form together in one step.
*Free choice of magnetizing direction-especially for multi-polar applications
*High dimensional accuracy-large quantity applications with minimum post-press machining.
*Thin-wall ring and complex shape magnets.
*High resistance to corrosion.

sonraíochtaí

Bonded NdFeB Magnets(Injection Molded)
Airíonna Maighnéadacha tipiciúla

Grád	Max. Energy Product		Remanence	Coercive Force				Rev. Temp. Coeff.		Working Temp.	Dlús
	(BH) uas		Br	Hc		Hci		Bd	Hd	Tc	D
	MGOe	kJ / m3	T	kOe	kA / m	kOe	kA / m	%/°C	%/°C	° C	g / cm3
BNI-2	0.8-3.0	6.4-24	0.2-0.4	1.5-3.0	120-240	7.0-9.0	560-720	-0.15	-0.4	130	3.5-4.0
BNI-4	3.5-4.5	28-36	0.4-0.49	3.1-3.9	247-310	7.2-9.2	573-732	-0.1	-0.4	180	4.0-5.0
BNI-6	5.2-7.0	42-56	0.49-0.57	3.9-4.8	312-382	8.0-10.0	637-796	-0.1	-0.4	150	5.0-5.5
BNI-8	7.4-8.4	59-67	0.57-0.63	4.8-5.4	382-430	8.5-10.5	676-835	-0.1	-0.4	150	5.0-5.5
BNI-6H	5.0-6.5	40-52	0.48-0.56	4.2-5.0	334-398	13.0-17.0	1035-1353	-0.15	-0.4	180	5.0-5.5

Bonded NdFeB Magnets(Compression Bonded)
Airíonna Maighnéadacha tipiciúla

Grád	Max. Energy Product		Remanence	Coercive Force				Rev. Temp.		Working Temp.	Dlús
								Coeff.
	(BH) uas		Br	Hc		Hci		Bd	Hd	Tw	D
	MGOe	kJ / m3	T	kOe	kA / m	kOe	kA / m	%/°C	%/°C	° C	g / cm3
BNP-6	5.0-7.0	40-56	0.52-0.60	3.8-4.5	304-360	8.0-10	640-800	-0.1	-0.4	140	5.3-5.8
BNP-8	7.0-9.0	56-72	0.60-0.65	4.5-5.5	360-440	8.0-12	640-960	-0.1	-0.4	140	5.6-6.0
BNP-10	9.0-10.0	72-80	0.65-0.70	4.5-5.8	360-464	8.0-12	640-960	-0.1	-0.4	120	5.8-6.1
BNP-12	10.0-12.0	80-96	0.70-0.76	5.8-6.0	424-480	8.0-11	640-880	-0.1	-0.4	130	6.0-6.2
BNP-8H	6.0-9.0	48-72	0.55-0.62	5.0-6.0	400-480	12 16 月 日	960-1280	-0.07	-0.4	120	5.6-6.0